Black Lithium Tantalate |
Standard Lithium Tantalate |
||
Standard Black |
Super Black |
||
| Bulk Resistivity (Ω · cm) | 2.30E+11 |
2.10E+10 |
4.50E+10 |
| Bulk Conductivity (&Omega-1; · cm-1) | 4.35E-12 |
4.76E-11 |
2.22E-15 |
| Surface Electric Potential(Note 1) /100mmφ(kV) | <0.35 |
<0.08 |
4.12 |
| Electrical Charge neutralisation (sec) | 3.5 |
1.5 |
∞ |
| Optical Transmission%(Note 2) | 65 |
<60 |
72 |
| Colour | Grey |
Dark Grey |
Colourless |
(1) Electrical charges due to temperature rising above room temperature to 95°C, at 4 inch LT wafer
(2) Transmission of 0.35mm thickness wafer (with both sides mirror polished) measured by 365nm wavelength
Lithium Tantalate 42° Y-cut |
||
Black |
Standard |
|
| Curie temperature Tc (°C) | 602.5±2 |
602.5±2 |
| SAW velocity | Unchanged |
4022 (note 3) |
| Coupling coefficient k2 | Unchanged |
7.6 |
(3) Surface skimming bulk wave
 |
 |
 |
 |
| Standard Black | Super Black | |
|---|---|---|
| Bulk Resistivity (Ω · cm) | 0.9E+11 ˜ 9.0E+11 | 1.0E+10 ˜ 9.0E+10 |
| Bulk Conductivity (Ω · cm-1) | 1.1E-11 ˜ 1.11E-12 | 1.0E-10 ˜ 1.11E-11 |
| Orientation | Diameter | Thickness | Surface Finish | |
|---|---|---|---|---|
(+) plane |
(-) plane |
|||
| 36 ° Y-cut | 76.2(mm) 100.0(mm) |
0.25(mm) 0.35(mm) 0.50(mm) |
Mirror Polished |
GC#1000 GC#1200 GC#2500 |
| 39 ° Y-cut | ||||
| 42 ° Y-cut | ||||
| 46 ° Y-cut | ||||
| 48 ° Y-cut | ||||
| X-cut | ||||
In addition to the above, we can apply our de-oxidation treatment to Lithium Tantalate wafers of any specification.